콘크리트 물-결합재비 및 광물질 혼화재가 전기-화학적 기법에 의한 부식 평가에 미치는 영향

Abstract

In this study, when concrete properties are changed by concrete mix proportions or blending of admixtures, the characteristics of electro-chemical method for corrosion assessment of the embedded steel are compared and its causes are analyzed. According to the results, when the ratio of corroding area was less than 10%, the half-cell method was affected by concrete properties. In the case of specimen blended admixtures, it is possible to assess the high-corroded steel qualitatively using the half-cell method. For the polarization resistance method, though the corroding area was less than 10%, it has not affected by concrete properties. However, in case of specimen blended admixtures, the corrosion level of steel was underestimated than OPC specimens having a similar corroding area.

본 연구에서는 콘크리트 배합과 혼화재 첨가에 의한 콘크리트 물성 변화가 매립 철근의 부식을 평가하는 전기-화학적 기법에 미치는 영향을 확인하고 그 원인을 분석하였다. 연구 결과 자연전위법은 철근의 부식면적이 10% 이하일 경우 콘크리트 내부 물성에 영향을 받는 것으로 나타났으며, 혼화재가 혼입된 경우에는 높은 부식상태의 철근에 대한 정성적인 부식평가가 가능하였다. 또한 분극저항법은 부식량이 10% 이하로 미미한 경우에도 콘크리트 물성의 영향을 받지 않았으나, 혼화재가 혼입된 경우에는 비슷한 철근부식면적의 OPC보다 부식정도를 과소평가하는 것으로 나타났다.