굴패각을 혼합한 콘크리트의 역학적 특성조사

Abstract

An experimental study was carried out to investigate recycling of an oyster shell, which is disposed in opendumped way at coastal oyster factory area. For this purpose, the chemical component and reaction of oyster shell with cement paste was examined. And, the characteristics of fresh concrete and hardened concrete was quantitatively investigated in terms of fineness modulus and blending rate of the crushed oyster shell. Test results show that the interaction between oyster shell and cement paste was not occurred and the workability of concrete decreases with decrease fineness modulus and increase the blending rate of the crushed oyster shell. And it was found that blending of an oyster shell caused not to reduce the 28 day compressive strength of concrete, and concrete blended with crushed oyster shells shows a rapid increase in strength with the blending rate. Elastic modulus of the concrete blended with crushed oyster shells decreases with increases the blending rate which the modulus reduced about 10% when oyster shells is blended up to the 20% of the sand substitution.

연안지역 굴양식장에서 발생하는 굴패각을 대량으로 처리하기 위하여,콘크리트의 잔골재 대체재료로 재활 용하기 위한 방법을 개발하는 연구를 수행하였다. 이를 위해 굴패각의 화학적 성분 및 시멘트와의 반응성을 조사하였으며 , 분쇄한 굴패각의 조립률과 대체율에 따른 굳지않은 콘크리트의 특성 및 경화한 콘크리트의 역 학적 특성을 정량적으로 검토하였다. 실험결과에 따르면 굴패각과 시멘트와의 사이에서 빈응은 일어나지 않았 으며,분쇄한 굴패각은 조립률이 작을수록,대체율이 증가할수록 작업성이 저하하였다. 그리고 굴패각의 혼합 은 콘크리트의 재령 28일 압축강도를 저하시키는 요인으로 작용하지 않았으며 굴패각의 대체율이 중가S수록 강도발현이 빠르게 나타났다. 또한 굴패각을 혼합한 콘크리트의 탄성계수는 굴패각 대체율이 증가할수록 감소 하였으며 모래단위량의 약 20%를 대체했을 경우에 콘크리트 탄성계수는 10%정도 감소하였다.