고화준설토의 역학적 특성과 식생 발아 특성

Abstract

In this paper, mechanical and germination characteristics of stabilized dredged soils were investigated to recycle dredged soil in eco-friendly manner such as waterfront construction. Non sintering binder (NSB), which was developed by using interchemical reactions between slag, high-calcium fly ash, alkali activator on the dredged marine clay, was added to dredged soil. Ordinary portland cement was also used for the comparison of two binders. Experimental tests such as flow test and unconfined compressive test were carried out to evaluate characteristics of stabilized dredged soil. Leaching test, pH measure, vegetation germination test were also conducted to consider environmental applicability. The unconfined compressive tests shows that unconfined compressive strength (UCS) also increases with the increase of curing time and mixed ratio. UCS of NSB mixtures were higher than those of OPC mixtures. Germination tests showed that germination and sprouting date are better in NSB mixture than OPC mixture. It can be explained that germination decreased as pH and 7-day strength increased.

본 논문에서는 준설토를 친수공간 조성과 같이 친환경적으로 재활용하기 위하여 고화준설토를 제작하였고, 역학적 특성과 식생 발아 특성을 분석하였다. 사용된 고화제는 고로슬래그 미분말을 기본재료로 고칼슘플라이애시 및 알칼리 복합 활성화제를 이용하여 제작한 고화제(Non Sintering Binder, NSB)이며, 비교 분석을 위해 포틀랜드 시멘트도 사용하였다. 고화준설토의 지반공학적인 개량 효과를 검토하기 위하여 유동성 시험, 단위중량 시험, 일축압축시험 등과 같은 다양한 실내 시험을 실시하고, 환경에 미치는 영향을 분석하기 위하여 중금속 용출과 식생 발아 실험을 실시하였다. 일축압축강도를 통하여 고화제의 함량이 증가할수록 모든 고화준설토의 강도가 증가하는 경향을 볼 수 있으며, NSB 고화준설토가 OPC 고화준설토보다 높은 강도를 나타냈다. 식생발아 실험 결과 OPC 고화준설토보다 NSB 고화준설토에서 발아 시기와 발아율이 우수하게 나타났다. 고화준설토의 pH와 7일 강도가 클수록 발아율과 발아 시기는 감소하는 경향을 보인다.